学兔兔 画 锂基膨润土的制备及其在铸造涂料中的应用 童树明，徐庆柏 (梯西埃姆 (安徽)机械有限公司，安徽 合肥 230601) 摘要：概述了锂基膨润土的制备过程。通过x射线衍射、差热分析及热失重分析，对钙基膨润 土和锂基膨润土的矿物结构和失水特征进行了分析，并测试了膨润土的悬浮度；同时介绍了采 用锂基膨润土作悬浮剂所制铸造涂料的配制工艺、性能和使用效果。结果表明，制备的锂基膨 润土在醇溶剂中悬浮性良好，可缩短铸造涂料的生产周期，并降低生产成本。 关键词：锂基膨润土；铸造涂料；悬浮性 中图分类号：TG221 文献标识码：A 文章编号：1673-3320(201 1)05-0008-04 Preparation of Lithium Bentonite and its Application in Foundry Coatings Tong Shuming，Xu Qingbai (TCM(An hui)Machinery Co．，Ltd．，Hefei 230601，Anhui，China) Abstract：The preparation of lithium bentonite was summarized．The mineral structure and dehydration feature of calcium bentonite and lithium bentonite were analyzed by XRD．DTA and TGA，and the suspension of samples was tested．The preparation，performance and useful effect of foundry coatings with lithium bentonite were presented．The results show that the lithium bentonite in alcohols solvent has better suspension．The foundry coatings have shorter production cycle and lower production cost． Kev words：lithium bentonite；foundry coating；suspension 醇基铸造涂料一般要用有机膨润土或锂基膨 具有较高的蒙脱石含量和阳离子交换容量。吸蓝 润土作悬浮剂。有机膨润土的制备过程是：用钙 量 (即亚甲基蓝吸附量)与蒙脱石含量的换算关 基膨润土作原料，经提纯后加入Na：CO s水溶液 系为： 中，通过离子交换反应转变为钠基膨润土，再加 w(蒙脱石)： 堕量×1o0％ f 1) 入季铵盐置换成有机膨润土。有机膨润土在醇基 0．442 一 涂料中分散性好，悬浮稳定性好。但是它必须经 根据JB／T 9227一l999规定的方法测定了一些 二甲苯或溶剂汽油引发，才能在醇液中膨胀。二 膨润土的吸蓝量。同时还用氯化铵一氢氧化铵法测 甲苯有毒，且气味难闻。另一方面有机膨润土的 定了膨润土的阳离子交换容量…。结果见表l。 价格为锂基膨润土的2倍以上。而锂基膨润土不 表1 几种膨润土的吸蓝量和阳离子交换容量 必使用二甲苯，只须用水引发。为此，本文研究 了锂基膨润土的制备方法及其