特大型球墨铸铁磨盘铸造工艺.pdf

学兔兔 Sep．2013 铸 造 V0I．62 N0．9 F0UNDRY ·835 · 特大型球墨铸铁磨盘的铸造工艺 秦大鹏，邹良利，张 琛 (大连华锐重工铸业有限公司，辽宁大连116300) 摘要：分别从铸型工艺、浇注系统、冷铁方案、冒口的设计、浇注工艺与产品的试制等方面，介绍了厚断面特大型 球墨铸铁磨盘的试制过程。通过理论值计算与MAGMA软件模拟完善了铸造工艺，降低产品的开发风险，从而成功 试制了特大型球墨铸铁磨盘。 关键词：磨盘铸件；铸造工艺；球墨铸铁 中图分类号：TG143．5 文献标识码：A 文章编号：1001—4977(2013)09—0835—03 Casting Process of Super-Large Ductile Iron Grinding Table QrN Da—peng，ZOU Liang-li，ZHANG Chen (Dalian Huarui Heavy Industry Casting Co．，Ltd．，Dalian 1 16300，Liaoning，China) Abstract：The development work of the super-large ductile iron grinding table was presented from following aspects：molding process，pouring system，chill design，riser position，pouring process and trial manufacture of the product．The casting process was improved and the development risk of the casting was decreased by the theoretical arithmetic and MAGMA simulation．And then the super—large ductile iron grinding table was successfully developed． Key words：casting grinding table；casting process；ductile iron 某大型球墨铸铁磨盘铸件 (图1)材质为QT400．1 8AR 根据铸件的重要工作面和大平面应尽量朝下或垂 (GB 1348--2009)。铸件净重为106．3 t，铸件外形最大 直安放原则f 2l及砂箱尺寸、造型难易程度，最终选择 轮廓尺寸为qb6 000 mrnx2 500 mm，主要壁厚190 mm， 6 000 mm大平面处分型，这样有利于模具制作、降 最大断面壁厚为540 mm。磨盘全身需做超声波检测 低造型难度、延长模具使用寿命。 (uT)和磁粉检测 (MT)，且要求较为严格，上下端 1．1．2 铸件机械加工余量 高应力区需满足欧洲标准二级要求，其他区域满足三 上端 3 600 mm大平面的加工量过大，将浪费金 级要求，力学性能以铸件本体附铸试块检测结果为依 属和机械加工工时，增加铸件成本；过小，则不能完 据，铸造难度较高[1]。又因工期要求为两个月内交货， 全去除铸件表面的缺陷 (铸件上表面易产生砂眼、夹 更是增加了生产难度。 杂缺陷)，达不到设计要求。为了保证铸件品质又不至 1 铸造工艺 于增加铸件成