铁型覆砂铸造在耐磨铸件领域应用.pdf

学兔兔 Aug．2015 Vo1．64 N0．8 铁型覆砂铸造在耐磨铸件领域的应用 刘同帮 ，沈永华 ， f1．浙江省机电设计研究院有限公司，浙江杭 I1 310002；2．浙江省先进铸造技术研究重点实验室，浙江杭州310002) 摘要：介绍了用于生产耐磨铸件常用的铸造工艺方法。对比各自工艺优缺点，认为铁型覆砂铸造工艺更适用于耐磨 铸件生产，尤其适合球铁材质耐磨铸件生产。详细介绍了铁型覆砂铸造生产耐磨铸件的工艺。 关键词：铁型覆砂；耐磨铸件；造型机；生产线 中图分类号：TG249．9；TG233 文献标识码：A 文章编号：1001—4977(2015)08—0731—04 Applk．ation of Sand—Lined Metal Mold Technology to Wear-Resistant Casting Field LIU Tong—bang 一．SHEN Yong—hua 0 (1．Zhejiang Institute ofMechanicalElectrical Engineering Co．，Ltd．，Hangzhou 3 10002，Zhejiang，China； 2．Zhejiang Province Key Laboratory ofAdvanced Casting Technology，Hangzhou 310002，Zhejiang，China) Abstract：The usual casting technology method to produce wear-resistant castings was introduced．The sand—lined metal mold technology is suitable for wear resistant casting by comparing the advantages and disadvantages ofeach process，especially for ductile iron material wear resistance castings．The sand—lined metal mold technologies ofwear resistance castings were introduced in detail． Key wo~ ：sand—lined metal mold；wear resistant casting；moulding machine；production line 耐磨材料分为金属耐磨材料和非金属耐磨材料。 操作为主，生产效率低，在球磨机衬板的生产中应用 在金属耐磨材料中，由铸造工艺制备的耐磨铸件又占 较多，一般不用于铸球生产；DISA造型线也就是射挤 有相当大的比例[1]。以铸造磨球为例，我国年产铸造磨 压垂直分型无箱造型线，最早由我国从国外引进，该 球达到了百余万吨[2]，在冶金、建材、电力、化工等行 线生产效率高，可达到120~200型／11[2]，但一次性投资 业，磨球都有大量的应用[3。。1，国内需求量和出口量也 昂贵，而且需要庞大的砂处理及除尘处理系统，运行 在逐年增加回。因此，与铸造磨球相关的国家标准和行 成本很高；壳型铸造主要采用叠箱工艺铸造磨球，其 业标准在不断提高 ，2010年4月 1日实施 的 占地面积小，工艺出品率较高嘲。但该工艺对型砂的透 GB／T17445--2009《铸造磨球国家标准》正式取代原 气性要求高，而且由于浇注后液态金属的静压头较高， 有的GB／T 17445—1998《铸造磨球国家标准》，成为行 低层铸球易产生粘砂缺陷，表面粗糙嘲，且耗砂量大， 业新规范嘲。修订后的 《铸造磨球国家标 达到了国 生产成本高。 外同类耐磨材料标准的先进水平l7]，这一标准定制水平 1。2 金