210吨顶底复吹转炉脱磷评价.pdfVIP

第十五届全国炼钢学术会议文集 210吨顶底复吹转炉脱磷评价 1 2 1 2 1 1 崔阳 南晓东 张莉霞 于文涛 冯军 朱立新 1 （首钢技术研究院, 北京 100043） （2 首钢迁安钢铁有限责任公司，河北 064404) 摘 要: 本研究分析了目前首钢迁钢公司炼钢厂转炉吹炼情况，重点讨论了 210 吨转炉脱磷能力。目前首钢 迁钢公司炼钢厂转炉吹炼水平较高，钢中终点磷含量能够稳定控制在低值，如 60ppm，回硫量也能够控制在 高水平，如 20ppm 。此外，终渣全铁含量过高以及终渣脱磷平衡度分散性大。 Estimation of Dephosphorization for Top and Bottom Blowing Converter of 210 t 1 2 1 2 1 1 CUI Yang NAN Xiaodong ZHANG Lixia YU Wentao FENG Jun ZHU Lixin 1 ( Shougang Research Institute of Technology, Beijing 100043) 2 ( Shougang Qian′an Iron Steel CO..LTD，Heibei 064404) Abstract: In the research, the metallurgical characteristics in the top and bottom blowing converter of 210 t for Shougang Qian’an Iron Steel CO..LTD were investigated, and the dephosphorization between slag and steel was mainly discussed. At present, the low concentration of phosphorus such as 60ppm in steel could be obtained, and the resulphurization control also reached a high level such as 20ppm. Moreover, the concentration of T. Fe was high and the data dispersability for the degree of phosphorus distribution equilibrium was large at the blowing end point. 1 前言 首钢迁钢公司炼钢厂现有三座 210吨（公称容量）顶底复吹转炉，全部采用自动化炼钢。炼钢自动化 控制系统包括静态控制和以副枪检测信息为基础的动态控制相结合的方法。随着副枪投入使用，转炉终点 钢水磷含量控制水平得到大幅提高。以 Q345B 为例，副枪投入前终点磷含量平均为 0.0185%，投入后磷含 量平均为 0.011%。以管线钢为例，钢中终点磷含量平均为 0.007%。在优化铁水预处理扒渣工艺、采用优 质低硫废钢和造渣材料以及控制废钢装入量等措施后，转炉终点硫含量控制水平也得到提高。 本文结合首钢迁钢公司炼钢厂转炉吹炼的现状，评价了转炉的脱磷能力。 2 转炉吹炼现状 2.1 钢水中碳含量和氧含量的关系 式