第十五届全国炼钢学术会议文集 45t 转炉炉况维护改进与应用 孟凡玉 （济南钢铁集团，济南 250101 ） 摘 要：转炉炉底上涨，转炉炉底下降，转炉熔池变形等炉型变化容易造成不利于冶炼过程控制,从而降低 了转炉炉龄和枪龄，易造成漏炉事故。通过采用“均衡”砌炉工艺，改进溅渣护炉工艺，补炉控制，生产工 艺控制，强化炉型测量，有效地保证了转炉运行的稳定，转炉补炉时间和耐材消耗大幅度降低，转炉炉龄达 到30000炉以上，降低炼钢生产成本。 关键词：氧气转炉；炼钢；炉衬护炉 The controlling and application of 45t Converters Lining MENG Fanyu Jinan Iron ＆ Steel Group Corporation ， Jinan 250101 Abstract: The rising and decline of converter bottom and the change of converter melting pool went against the controlling of smelting process,the age of converter and oxygen gun was reduced ,and converter leak taked place easely.through aplling the technics of equilibria bricklaying ,improving the technics of protecting furnace by bespattering slag ,controlling production techinics , and strengthening the measure of converter shape, the stabilization of converter running was ensured efficiently,the time and the cost of repair furnace was reduced enormously,the converter age reach 30000,the cost of steal-making was reduced. Key words: oxygen converter，steelmaking，converter Maintenance 1 前言 济钢第一炼钢厂现有 45t 转炉 4 座，通过扩容改造后转炉有效容积为 32m3，目前单炉出钢量 50 t 左 右，年产量 400 万 t。随着生产节奏的提高和高质量标准要求的品种钢特别是低 C 高合金量钢种比例的增 加，转炉炉衬维护特别是炉役中后期炉型控制对生产的稳定和品种质量提高的影响越来越明显，转炉炉型 控制不当一方面不利于冶炼过程控制，造成吹炼过程喷溅返干现象严重，炉口氧枪烟道粘钢现象严重，大 大增加炼钢钢铁料和造渣料消耗成本，同时降低了转炉炉龄和枪龄，极易造成漏炉等恶性事故，危害生产 稳定和设备安全，另一方面由于炉型不均匀造成终点钢水温度、成分偏差较大，极易造成成分出格和低温 事故，特别是限制了低 C 品种钢的生产开发，影响了正常生产组织和品种计划的兑现。为此，通过提高转 炉炉型控制工艺系统开发来稳定转炉炉型，对促进炼钢生产稳定发展具有重要意义。 2 转炉炉型变化及成因 2.1 转炉炉底上涨 2.1.1 转炉炉底上涨危害 炉底上涨造成转炉有效容积减小(见图 1)，根据计算，35t转炉炉底每上涨 100 mm，转炉有效容积减小 0.75 m3，相应降低转炉有效容积 2.5%，炉底严重上涨后，转炉操作过程中喷溅现 象加重，降低了金属收得率，增加了钢铁料消耗，同时由于喷溅严重