YAG激光与GTAW 复合焊接铝合金.pdfVIP

2004 年第 38 卷№11 43 YAG 激光与 GTAW 复合焊接铝合金 施 　晔 上海交通大学 摘 　要 :研究了 YAG 激光、GTAW 电弧复合焊接铝合金时各种规范参数对焊缝成型的影响规律,探讨激光与电 弧的复合作用机理。结果表明 ,采用 YAG 激光 + GTAW 复合工艺焊接铝合金具有焊缝成型美观、热影响区小等优 点 ,与 GTAW 焊接相比 ,焊速显著提高 ,可以显著增加熔深 ,达到采用小功率激光焊机实现铝合金的焊接目的 , Laser 、GTAW 是铝合金焊接理想的工艺方法。 关键词 :YAG 激光 , 　GTAW , 　焊接 , 　铝合金 YAG LASER and GTAW Compound Welding Aluminum Alloy Shi Ye Abstract : The effect on welding depth profile under various welding parameter while using YAG LASER、GTAW 、GTAW + LASER to weld aluminum alloy is studied. The mechanical properties of LASER reacting to arc are discussed. The result shows that the welding line profile is better and HAZ is smaller by YAG LASER + GTAW. The welding speed and penetration are im proved prominently comparing with GTAW to realize aluminum alloy welding with low power LASER machine. Laser、GTAW are the perfect methods for aluminum alloy welding. Keywords :YAGLASER , 　GTAW , 　welding , 　aluminum alloy 激光的吸收能力 ;其二 , 由于 GTAW 电弧焊缝宽,激 　　1 　引言 光允许接头间隙增加 ,GTAW 电弧加上激光束焊,可 铝及铝合金激光焊接技术是近十几年来才发展 使焊缝熔深增大 ;其三 ,可使 GTAW 的电弧稳定 , 当 起来的一项新技术 ,铝合金材料大量用在地铁轻轨 GTAW 焊的速度加快时 , 阳极斑点不稳定会产生电 和汽车制造领域。铝合金的焊接技术也引起各国科 弧飘移 ,若并用激光焊束 , 则 GTAW 的电弧能借助 研部门和工程技术人员的重视。铝合金独特的性能 激光引起的等离子体而得以稳定 , 因此采用Laser - 决定了其焊接特点 ,即必须采用能量集中的热源 ,如 GTAW 联合焊接技术可以对铝进行大熔深和高速焊 GTAW 焊、MIG 焊及LASER 焊。与传统的 GTAW 焊、 接。 MIG 焊相比 ,激光焊接是一种功能多、适应性强的精 　　 2 　GTAW + 激光焊的试验设备和工艺 密焊接方法。由于功率密度高 , 除具有焊接时热输 入量低、焊接热影响区小、焊接变形小外 ,还具有质