南钢板坯连铸轻压下技术的研究.pdfVIP

第十五届全国炼钢学术会议文集 南钢板坯连铸轻压下技术的研究 田陆，赵磊，江兵 镭目公司北京研究所 北京 100080 摘要：主要介绍了南钢 2#连铸机的静态轻压下实验，通过对连铸机了解，用理论计算和实际射钉的方法确 定了连铸板坯的凝固终点.改造了南钢 2#机的三个机架，使它具有了轻压下功能。通过不断的实验最终确定 南钢 2#连铸机最好的压下位置、压下量和压下率改善了板坯的中心偏析和中心疏松，提高了南钢板坯的质 量。 关键词：轻压下；板坯连铸：凝固末端 Research on soft reduction technology for slab continuous casting at Nanjing steelwork Tianlu, Zhaolei, Jiangbin Beijing Institute of Ramon Corporation Abstract: This paper presents a static soft reduction experiment of 2 # continuous casting machine at nangang,with the theoretical arithmetic and nail-shooting technique that determining the solidification end of the slab, three fan-shaped section wrere altered and making it has soft reduction function.Through constant experimentation,we determined the best place of reduction ,the best scale of reduction and the best velocity of reduction, reduced the center segregation and looseness, improved the quality of the Nanjing Steel slab. Key words: soft reduction;slab continuous casting ; solidification end of the slab 1 前言 连铸板坯中存在着中心偏析、中心疏松等缺陷，降低铸坯中心偏析目前较为成熟的技术有电磁搅拌技 术、低过热度浇铸、二次冷却弱冷技术和凝固末端轻压下技术。南钢2#连铸机通过了镭目公司的改造，实 现了静态轻压下功能。轻压下实验表明：镭目公司的轻压下技术使南钢连铸坯的中心偏析得到较好的控制， 同时铸坯中心疏松亦得到改善。 2 轻压下技术的原理 连铸轻压下技术是在连铸坯液芯末端附近施加压力，产生一定的压下量来补偿铸坯凝固的收缩量，消 除或减少铸坯收缩形成的内部空隙，让枝晶间富集溶质的剩余液相仍保留在原来的位置，防止向铸坯中心 横向移动形成偏析，同时轻压下的压下作用使液芯钢液沿拉坯的反向流动，使中心钢液重新分配，从而使 中心凝固组织更加致密，成分更加均匀，起到降低中心碳偏析和改善中心疏松的作用[1]。轻压下最关键 的工艺参数为压下区间和压下量，解决这两个问题是轻压下成功的关键[2]。 3 设备参数介绍 铸机基本参数： 台数 1台 流数 1流 连铸机半径 Ｒ＝5.7／7.2／11.0／21.0米多点矫直 浇注断面 180×800～1200mm2 定尺长度