PVC共混增韧改性研究进展.doc

第34卷增刊 塑料工业 2006年5月 CHINA PLASTICS INDUSTRY · 65 · PVC共混增韧改性研究进展 高风芹。宁荣昌” (西北工业大学理学院，陕西西安710072) 摘要：阐述了近年来国内外聚氯乙烯(PVC)共混增韧改性的研究进展；介绍了PVC化学改性和物理改性；探讨 了PVC弹性体共混增韧改性和刚性粒子共混增韧改性，尤其是纳米粒子共混增韧改性，指出了PVC共混增韧改性的 研究前景及发展方向。 关键词：PVC；共混增韧改性；弹性体；刚性粒子 Advance in Study of PVC Modified by Blending Toughening Method GAO Feng·qin，NING Rong—chang (School of Natural and Applied Sci．，Northwestern Polytechnieal University，Xi’all 710072，China) Abstract：The advance in the study of blending toughing modification of PVC in recent years is reviewed，and the modifications by means of chemical and blending methods are introduced。The blending toughing modification of PVC by elastomer and rigid particles are discussed，with the emphasis on the modification by nano—meter particles． The prospects for the study and the trend of the development of the blending toughing modification of PVC are point- ed out． Keywords：PVC；Blending Toughing Modification；Elastomer；Rigid Particle 聚氯乙烯(PVC)树脂是由氯乙烯单体聚合而成 1与弹性体共混增韧改性 的热塑性高聚物，是最早工业化、产量位居第二的通 PVC与弹性体共混增韧改性是目前研究最多，理 用塑料，具有阻燃、耐磨、耐酸碱、绝缘等优良的综 论也较为成熟的一种增韧方法。用于增韧PVC的弹 合性能和价格低廉、原料来源广泛的优点，被广泛应 性体主要有代表“网络增韧”机理的NBR、CPE、 用于农业、化工、建筑等各个部门。然而，纯硬度 EVA、TPU和代表“剪切一屈服银纹化”机理的 PVC的缺口冲击强度只有3—5 kJ／m2，其拉伸强度与 ABS、MBS、ACR、Elvaoy741等。 工程塑料接近，但其低温冲击强度低于ABS；而软质 1．1 PVC／NBR共混增韧改性 PVC的增塑剂迁移性大，使用过程易发生脆裂。根据 NBR是增韧PVC最早商品化的改性剂，因其耐 Vincent关于聚合物脆性．韧性断裂行为的表征，PVC 油、耐老化、耐腐蚀且与PVC相性好等优点而倍受 属于硬脆材料 。PVC具有冲击强度低、热稳定性差 青睐。Mano等¨1J发现PVC与NBR在150℃下进行机 等缺点，限制了其在性能要求较高领域的发展，因此 械共混时，两相之间具有较好的相容性，体系交联结 需要进行增韧改性[2-3 J。 构的存在使体系具有良好的综合力学性能。随着 通过化学改性和物理改性两种方式可以改善PVC NBR含量的增大，体系的断裂伸长率迅速增大，但 的上述缺点。化学改性是在PVC链段上引入柔性链 拉伸强度有所下降。在PVC／NBR(质量比)为75／25 节单元，以提高其韧性，但化学改性由于经济和技术 时，体系的拉伸强度为32 MPa，断裂伸长率达 的限制，研究成果不多。物理改性是改性剂与PVC 175％，表现出较好的韧性。Liu Z H等[12-13 J将NBR 共混，起到增韧的作用，是一种简单易行、经济实 相呈准网络态分布于PVC中，其增韧效果要优于简 用的方法，尤其是纳米增韧改性，已成为国内外研究 单共混。Schwarz H F等发现羧酸化的丁腈橡胶(XN． 的热点[4-10 J。本文主要阐述了PVC共混增韧改性的研 BR)对PVC的增韧效果比NBR的要好，共混物的冲 究进展。 击强度、拉伸强度、模量均比NBR更高，且耐磨性 *联系人029—884741