b8造制备ZL101铝合金导体的组织和导电率研究.pdf

2010 中国铸造活动周论文集 差压铸造制备ZL101铝合金导体的 组织和导电率研究 于宝义，陈月蕾，刘春雨，韩涛 （沈阳工业大学 材料科学与工程学院，沈阳 110178） 摘要：本研究采用差压铸造和重力铸造方法制备了 ZL101试样，利用金相显微镜和扫描电子显微镜能谱对 铝合金导体的组织进行了分析。结果表明，差压铸造工艺下的显微组织细密，性能优良。经过 T5 热处理 后，显微组织出现了球化与细化。力学性能得到明显的改善，导电率达到 45%IACS。 关键词：差压铸造；金相；ZL101 Effect of Counter-pressure Casting on Microstructure and Mechanical Properties of ZL101 Aluminum Alloys YU Bao-yi ，CHEN Yue-lei，LIU Chun-yu ，HAN Tao （School of Materials Science and Engineering, shenyang University of Technology, shenyang 110178） Abstract ：Counter-pressure casting and gravity casting ZL101 test simple was prepared for this study. metallurgical structure and alloy performance was analyzed by metallographic microscope and scanning microscope, the results showed that the counter-pressure casting process gets fine morphology and proformance. After T5 heat treating, microscopic structure was sharply globurizing and refining. Parameters such as mechanical properties get the desired impact, and the specific conductance achieved 45% IACS, was an ideal microstructure and alloy properties. Key words：counter-pressure casting; metallographical; ZL101 随着科学技术的不断发展，对铸件的品质要求越来越高，因此出现了一种新的铸造方法，差压铸造法 [1]。差压铸造是在铸型外罩以密封罩，同时向坩埚内和密封罩内通入压缩空气，并使坩埚内压力高于罩内 的压力，坩埚内的熔融金属在压力差作用下，经升液管从型底注入铸型，并在压力下进行结晶的铸造方法。 铸型内的金属液在高压下结晶凝固的方法使铸件得到较致密的结晶组织，提高了铸件的机械性能。据资料 介绍这种工艺与一般铸造方法相比，使铸件强度提高约 25％，延伸率提高约 50％。本文主要对比了同种 材料在差压铸造下与重力铸造下的组织性能[2]。 1 材料及试验方法 1.1 实验材料 研究中采用的实验材料 Zl101 属于 Al-Si 类铸造铝合金，含有较高的 Si，少量的 Mg，具有良好的铸 造工艺性能、机械性能和抗腐蚀性能，可用于砂型铸造、金属型铸造和压力铸造。实验合金成分如表 1， 扫描电镜能谱分析如图 1 所示。 1 2010 中国铸造活动周论文集