1-3 合金的结构.ppt

* (0 0 1) APB (a)Periodic arrangement of D023 （b）The equivalent structure of a D023 unite cell (c) An APB is intruded between two D022 cells (d) two D022 cells The structure included in the blue box in figure (a) is the unite cell of D023, and simply extends the D023 structure along [0 0 -1] direction according to the periodic arrangement of crystal, one gets a structure that equal to the unite cell of D023 (Shown as figure (b)). Figure (d) consists of two D022 unit cells, and we introduce an APB between the D022 cubes getting figure (c). Ignoring the occupancy difference of the dark blue sites and the light blue sites in figure (c), and comparing figure (c) with (d), we find that the two crystal structures are absolutely same with each other, which mean that the structure transition from D022 to D023 is true. * L12和DO22结构之间的转变 (a) L12晶胞 (b) 每两个L12结构的(001)面上插入一个反相畴界形成图(c)所示结构, 和D022结构构造相同 (c) D022单胞 * 体心立方有序衍生结构 B2，AB型 NiAl、FeAl DO3，A3B型 Fe3Al、Fe3Si、 Fe3(Al、Si) L21，A2B型 Cu3MnAl、Ni3AlTi C11b，AB2型 MoSi2 * 密排六方有序衍生结构 DO19，A3B型：Ti3Al DOa、A3B型：Cu3Ti、Ni3Nb、Ni3Ta 密排六方晶胞及其衍生结构 * FCC衍生结构 BCC- B2结构 HCP- D019结构 L12 D022 L10 Ni3Al, Ni3Ge, Cu3Au,Ni3Fe, (Co,Ni)3(Al,Ti) Ni3V, Ni3Cr, Al3Ti，TiAl3 NiAl , TiAl, CuZn, CuAuⅠ TiAl, NiAl, CuZn, FeAl, AuTi, CoFe, CuAuⅡ Ti3Al, Co3V, Fe3Ge 常见金属间化合物及其结构 * 金属间化合物结构材料典型 Ni-Al金属间化合物 Ni3Al：L12，B、Zr提高塑性、Cr提高抗氧化性、Mo提高高温强度 NiAl：B2，形成NiAl+Ni3Al双相组织，起强韧化作用 Fe-Al系富铁金属间化合物 Fe3Al：D03，Cr固溶提高塑性，B抑制脆性，Nb、Mo、C强化合金提高高温强度 FeAl：B2，水汽环境下较脆，B抑制环境脆性、有产生热空位倾向、淬火引入空位导致硬化 Ti-Al系金属间化合物 Ti3Al：DO19，Nb增加强度和塑性，V、Mo、Sn、Zr提高高温强度 TiAl：L10、B2，Cr、Mn、V提高塑性，B细化晶粒 * 致 谢 本课件的基本内容引用国内外学者的专著、教材、论文、课件、报告、网页等，仅列出小部分参考形式，其余并未逐一注释，向相关学者表示感谢。 特别感谢陈铮教授分享授课经验、参考资料和课件。 张静 * Thanks for your attention ! 谢　谢　大　家 ！ * * 西北工业大学 材料学院 陈铮 本科生学位课 金属材料学 材料学院 陈铮 本科生学位课 金属材料学 * 第三章?合金的结构与材料的性质 * 把由一种金属元素与其它金属原子或非金属元素组成的具有金属性质的物质称为合金。 组成