毕业设计（论文）-年产10万吨ABS树脂接枝粉料车间工艺设计精选.doc

毕业设计摘 要 ABS树脂是聚丁二烯橡胶、单体苯乙烯和丙烯晴的接枝共聚物，它兼具三种组分的共同性能，无毒、无臭、耐冲击、质硬、尺寸稳定、耐化学腐蚀、电性能良好、易于成型加工，表面光洁和容易着色。ABS树脂是目前产量最大、应用最广的热塑性工程塑料。 目前世界上ABS树脂合成仍广泛采用的是乳液接枝掺混法。该法是用乳液接枝法生产高胶的ABS接枝粉料作为中间品，将中间品于本体AS聚合物进行掺混。挤出造粒生产ABS树脂。该法工艺成熟、流程短、设备少、生产品种多、适宜大规模生产。 本设计主要完成了ABS接枝粉料段的工艺流程设计、反应釜设计、车间布置设计、编制了设计。 关键词：ABS树脂、工艺、乳液接枝掺混法 Abstract ABS resin is Polybutadiene Rubber, styrene monomer and acrylonitrile graft copolymer, it combines three components of common, non-toxic, odourless, resistant to shocks, the quality is hard, good dimensional stability, chemical resistance, electrical properties, ease of forming, the surface is smooth and easy coloring. ABS resin is by far the most productive, the most widely used thermoplastic plastics. Synthesis of world ABS resin emulsion grafted mixing method is widely used. This Act was produced using emulsion grafting grafting of ABS high glue powder as an intermediate product, intermediate in the ontology AS polymer blending. Extrusion granulation production of ABS resin. The Act less short mature technology, process, equipment, production, varieties, suitable for mass production. This design ABS grafted powder process design, plant layout design, reactor design, preparation of design specifications. Keyword: ABS , craft , lotion copolymeriztion. 目录3.2.2.1 PBL的接枝聚合机理 PBL的链节中有双键存在，也有α-氢存在，都容易被自由基攻击形成活泼接枝点。这些活泼性接枝点实际上是大分子链自由基，可以引发ST,AN进行接枝反应，产生接枝橡胶。和一般的自由基聚合一样，接枝共聚也经历了引发剂的分解，大分子链自由基的形成，接枝反应发生和、及链增长，链终止等四步反应。 3.2.2.2 接枝胶乳的凝聚机理 这是ABS接枝粉料生产中重要的一步工序。接枝聚合所得到的胶乳是稳定的，胶粒的直径在0.01-5um之间，粒子表面吸附了一层乳化剂，分布在乳胶粒子与水介质的界面之间，亲油基团向内附于胶乳粒子表面，亲水基团向外与水介质渗透形成水化层。胶乳粒子对水作相对运动，滑动面不在胶乳粒子表面而在水化层表面。同时乳胶粒子向水介质扩散过程中，形成扩散层，其电势逐渐以指数速度下降。滑动面电位为ε电位，也叫动电电位。胶乳粒子电荷越多，ε电位越大，胶乳越稳定。ε电位的大小决定着胶乳体系的稳定性。 凝聚过程就是用相反电荷降低ε电位，破坏胶乳的稳定性，使胶乳凝聚出聚合物。一般通过三种途径： 电荷中和 高分子絮凝剂的吸附架桥 表面吸附 良好的凝聚标志是：凝聚粒子大，均一而不结块。干粉假相相对密度在0.4以上，干粉呈白色，离心洗涤的进料比较大，洗涤工序通常。 3.2.2.3 干燥 离心洗涤后湿粉的含水量一般在35%左右。如果采用湿粉挤压造粒机造粒，那么就不用干燥了。如果用干粉挤压造粒机，则必须干燥至含水量≤1%。 3.3 生产工艺过程 3.3.1 简述 ABS粉料的生产工艺过程一般分为三步：