《杨木纤维长度研究》.docVIP

摘　要：对5年生人工林杨树107杨（Populus×euramericana cv.‘74/76’）木材的纤维长度、纤维宽度、纤维壁厚、纤维长宽比和壁腔比等纤维形态特征指标进行了系统地测试。结果表明，在径向上，木材纤维长度、纤维壁厚、长宽比的变异都是自髓心向外逐年增大；而纤维宽度自髓心向外逐年增大，至第4年达最大值，此后再减小；壁腔比变化幅度不大。纤维形态各指标的径向变异均大于轴向变异。关键词： 欧美杨107杨　木材纤维　形态分析Morphological Analysis on the Woody Fiber of Populus×euramericana cv.“74/76”Zhang Li　Zhao Rongjun　Fei BenhuaAbstract:??Key fiber morphological features, fiber length, fiber width, cell wall thickness, ratio of length to width and ratio of cell wall thickness to lumen diameter of 5-year-old Poplar 107(Populus×euramericana cv.‘74/76’)were determined and analyzed. The results were as fllows. In the radial variance: from pith outward, the fiber length, the cell wall thickness, the ratio of length to width all increase year after year; while the fiber width increases year after year, reaches maximum at the 4th year and then decreases; the ratio of cell wall thickness to lumen diameter mostly fluctuates above or below an axis. The radial variance of the wood morphological properties is larger than these of the axial variance. Keywords: Populus×euramericana cv.“74/76”, woody Fiber, morphological Analysis　　为了改变木材资源日益缺乏的现状，世界各国均加大了人工林培育的力度。我国是人工林发展较早且面积较多的国家。但是，由于当初培育人工林时没有研究木材材性与林木培育的关系，未能按照用材部门对木材材性的要求营造人工林，以致现在已成林的工业人工林木材很难适应市场的需求，在缓解木材供需矛盾中不能起到应有的作用。目前摆在我们面前的问题有二：一是现有的低质人工林木材怎样利用？二是未来优质人工林木材怎样营造[1]？而解决这些问题的关键着手点是木材材性及其早期预测研究。　　杨树是我国重要的速生丰产林和短周期工业用材林首选树种，对杨树的木材性质及其变异进行研究具有重要的意义。纤维形态特征的大小直接决定着木材的物理、力学性质，影响着木材的加工利用，尤其是制浆造纸方面，纤维形态特征大小关系着制浆造纸的质量好坏[2]。本文通过对欧美杨107杨纤维形态的分析，以期对其林木的定向培育与木材加工利用提供科学依据。1??材料与方法1.1 试材采集　　试验林选自北京郊区密云的杨树人工林地，土质为沙壤土。取样方法按照国家标准[3]进行，选取5株标准样木。样木基本情况见表1。 下载 (32.68 KB) 2010-6-24 09:50 1.2 试材制作　　　每株样木伐倒后,分别在1.3、3.3、5.3m处各取5cm厚圆盘两个，标明南北向及序号，气干后备用。1.3 试验方法　　试样的制备及测试方法参考文献[4]。1.4 数据处理方法　　主要原始数据经Excel软件统计处理，进行方差分析、回归分析和相关分析，对纤维形态各指标的径向变异、轴向变异进行比较分析。2??结果与分析2.1 纤维长度的变异　　图1显示107杨不同高度纤维长度的径向变异规律，从图中可以看出人工林107杨不同高度纤维长度的径向变异趋势基本类似：即从髓心向外逐年增加。在株间和同一高度的纤维长度径向变异有一定的差别，树干5.3m处的变异系数最大,为23.81％，变异范围为1843.79～484.4μm(表2)。5年生的107杨木材纤维