铝酸钠溶液中和制备纳米丝状氢氧化铝 1,2 1 1 1 李艳 , 张亦飞, 杨超 , 张懿 (1. 中国科学院过程工程研究所，北京，100080 2. 中国科学院研究生院，北京，100049) 摘 要: 研究了铝酸钠溶液的盐酸中和过程对氢氧化铝晶体的形貌，晶型和铝酸钠溶液分 解率的影响。实验结果表明，随着反应体系pH 值的下降，氢氧化铝的形貌在不断发生变化， 且 pH 值越大，晶体越大；不论 pH 值如何变化，氢氧化铝的晶型总是 gibbsite；铝酸钠溶 液的分解率随溶液pH 值降低而升高。 关键词：铝酸钠；氢氧化铝；中和；纳米丝 中图分类号：TQ 16.1 文献标识码：A Fibre-like aluminium hydroxide nanoparticles prepared by neutralization of sodium aluminate solution LI Yan1,2 1 1 1 ，ZHANG Yifei ，YANG Chao ，ZHANG Yi ( 1. Institute of Process Engineering, Chinese Academy of Sciences. Beijing, 100080，China 2.Graduate University of Chinese Academy of Sciences. Beijing, 100049,China) Abstract: Procedure for precipitating aluminium hydroxide from sodium aluminate solution was investigated, and hydrochloric acid was used as neutralization agent. Effect of pH on the crystal morphology, crystal type and sodium aluminate decomposition rate were studied. The experimental results showed that the crystal morphology of aluminium hydroxide varied with the decreasing pH value of the solution, in addition, the higher the pH value the larger the crystallites of the precipitates; no matter how the pH value changed, the precipitates always were gibbsite; and the decomposition rate increased with the decrease of the pH value. Key words: sodium aluminate; aluminium hydrate; neutralization; nano-fibre 基金项目：国家重点基础研究计划（2007CB613501 ） 作者简介：李艳，博士研究生；电话：010 E-mail: guigongliyan@163.com 通讯作者：张亦飞, 博士； 电话：010 E-mail: yfzhang@ 氢氧化铝粉末作为阻燃剂在电工、建筑材料、塑料和橡胶等行业中得到了广泛应用。目 前，常用的阻燃剂可分为三种：反应型阻燃剂，有机添加型阻燃剂和无机添加型阻燃剂。反 应型阻燃剂热稳定性好，毒性低，对高聚物的其它性能影响小，但其工艺复杂，成本较高； 有机添加型阻燃剂往往会带来阻燃制品的发烟，毒气释放等环境和使用安全问题；无机添加 型阻燃剂具有热稳定性好，毒性低，甚至无毒，不产生腐蚀气体，储存过