C65高性能砼研究与工程应用.docVIP

C65高性能砼的研究与工程应用 　　摘要：本文主要论述高性能混凝土的特性及高性能混凝土原材料选用的技术要求，着重阐述了高性能混凝土关键材料水泥、骨料、外加剂及活性掺合料的技术要求，详实列出了C65高性能混凝土的配合比数据，论述了高性能混凝土在生产与施工中须重视的质量控制措施。 　　关键词：高性能混凝土活性掺合料混凝土水灰比混凝土坍落度。 　　liuWenqing 　　Construction Engineering Co., Ltd. Sichuan Hui Rong Sichuan. Ziyang641300 　　Abstract:This text is main to discuss the characteristic and the high performance concretes original material of the high performance concrete to choose the technique request for use, emphasizing to elaborate the high performance concrete valve key material cement, bone to anticipate, the in addition and the technique request of the live in addition material, thorough listed the data of mix proportion of the C65 high performance concrete, discuss the high performance concrete at produce to control the performance with the mass that under construction beard value. 　　Key word:The high performance concrete, live in addition material, concrete water cement ratio, concrete collapses to fall the degree. 　　1、工程简介 　　深圳茂业时代广场是一座超高层建筑，工程位于深圳市南山区文心二路侧，南侧为海德二道，西边是南山书城。建筑总高度：127.5m,总建筑面积: 90065.62m2。地下室：3层，塔楼：24层,裙楼：9层,塔楼为钢框架筒结构，底层柱截面为:1.5m*1.5m钢筋混凝土柱、核心筒部分柱子与核心筒转角部分增加H型钢钢结构骨架，外包高强混凝土。塔楼9层以下柱、核心筒墙混凝土设计强度等级为C65，该工程的技术难点之一是柱、墙C65高性能混凝土的配制与施工。 　　2、高性能混凝土的特性 　　高性能混凝土是在大幅度提高常规混凝土性能基础上，采用现代混凝土技术，通过优选原材料并在混凝土中加入足够数量的活性掺和料和高性能外加剂的一种新型高技术混凝土。它具有高强度、高耐久性和优良的工作性三个特点。由于以上特性，高性能混凝土在现代高层建筑中得到广泛应用，并极大地促进了现代超高层建筑的发展。 　　 　　3、高性能混凝土原材料技术性能要求 　　3.1水泥:水泥在混凝土中起着凝结作用，水泥标号高低、质量优劣对高性能混凝土的特性有极大影响。常规下,高性能混凝土须使用525号以上普通硅酸盐水泥或中热硅酸盐水泥。根据本工程的情况,工程择优选择了福建“顺昌”PO.525炼石水泥作为C65高性能混凝土原材料，检验资料显示:炼石P.O525水泥28天平均强度为:62Mpa，该水泥矿物成分C3A含量低,质量稳定,适宜配制高性能混凝土。该水泥主要矿物成份:C3S为40-55%,C2S为20-30%,C3A为6-8%,C4AF为10.5-12.5%,R2O为0.4-0.6%。水泥的各项技术性能指标符合配制高性能混凝土要求，其技术性能指标见表1 　　表1 P.O525炼石水泥技术性能指标 　　检验项目 凝结时间 　　(min) 抗折强度 　　(Mpa) 抗压强度 　　(Mpa) 细度 　　(%) 安定性雷氏法 　　(mm) SO3含量 　　(%) 烧失量 　　(%) 　　 初凝 终凝 3d 28d 3d 28d 　　检验结果 96 160 6.2 9.1 36.6 66.6 1.9 1.0 1.89 2.49 　　3.2河沙:高性能混凝土用砂要严格控制含泥量和有害杂质，沙的含泥量不得超过3%，云母、轻物质、硫化物、及硫酸盐含量不得大于1%。要合理调整砂率，细度模数应在2.8以上，为保证高性能混凝土的可泵性，