硫酸盐侵蚀过程中石相生成条件的研究.docx

 PAGE \* MERGEFORMAT 9  PAGE \* MERGEFORMAT 1 硫酸盐侵蚀过程中石膏相生成条件的研究 The condition of the formation of gypsum in sulfate attack 内 容 摘 要 硫酸盐侵蚀是影响混凝土耐久性的一个重要因素，实际工程由于硫酸盐侵蚀引起的混凝土结构未到服役寿命就产生各种破坏的案例非常多，为了防治硫酸盐侵蚀对基础设施的腐蚀破坏，确保安全生产，对混凝土硫酸盐侵蚀的相关问题进行深入的探讨和研究尤为必要。本文在国内外研究的基础上，对硫酸盐侵蚀中的石膏型硫酸盐侵蚀做了进一步的研究，设置了CaO-SO3-Na2O-H2O体系在不同pH 值条件下进行反应，以此来模拟硫酸盐侵蚀中石膏的形成环境，进而探究石膏的形成条件。 关键字：硫酸盐 石膏相 pH Abstract Sulfate attack is an important factor which influences the durability of concrete. The cases of damaged concrete before its service life due to sulfate attack are often recorded in the actual structures. In order to prevent the damage caused by sulfate attack to the infrastructure, and ensure the safety in production, a further study and research on sulfate attack in concrete is necessary. In this paper, a further research on the problem of gypsum in sulfate attack on the basic of research results at home and abroad is carried out. In order to simulate the forming of gypsum in sulfate environment, a CaO-SO3-Na2O-H2O system is set to react and form gypsum under the condition of different pH value. Key words: sulfate attack gypsum; ph  硫酸盐侵蚀过程中石膏相生成条件的研究 The condition of the formation of gypsum in sulfate attack 混凝土是重要的建筑材料 , 用途十分广泛。在正常使用条件下，混凝土的耐久寿命一般为 50～70年，高性能混凝土可达100年以上[1]。然而现实中混凝土多孔的材料特性，为自然界中各种离子的侵蚀提供了天然通道，因此耐久性不足是常用的普通混凝土的主要缺点之一。水泥混凝土耐久性指的是处于一定环境条件下的混凝土构件抵抗环境中的有害作用而长期持久服役的能力。因环境作用的多样性，对混凝土耐久性的研究涉及的内容很多，其中最主要的有混凝土钢筋锈蚀的防护、混凝土防冻融循环作用损伤、硫酸盐侵蚀机理、碱集料反应病害治理等[2]。 硫酸盐侵蚀是影响混凝土耐久性的一项重要因素，同时也是影响因素最复杂、危害性最大的一种环境水侵蚀[3]。引起硫酸盐侵蚀的因素比较复杂，对混凝土构件造成的危害也较大。硫酸盐侵蚀按照硫酸根的来源可以分为内部硫酸盐侵蚀和外部硫酸盐侵蚀。内部硫酸盐侵蚀主要是由于采用的含有硫酸盐的集料在混凝土内部与水泥水化产物发生反应而引起内部侵蚀和由于高温养护出现的延迟钙钒石膨胀而引起的硫酸盐侵蚀；通常所说的硫酸盐侵蚀主要是指外部环境中硫酸根离子与硬化水泥浆体中的水化产物发生反应导致混凝土结构产生破坏。通常来说，引起混凝土结构破坏的硫酸盐侵蚀主要是由于遭受了含硫酸盐的土壤、地下水、流动水等的腐蚀作用，因此外部硫酸盐侵蚀是一直是国内外关注较多并研究较为热门的问题。当混凝土结构暴露在含有硫酸盐的环境中，外部的硫酸根离子通过扩散、迁移进入混凝土结构，并与硬化水泥浆体中的水化产物发生反应，最终导致混凝土结构发生破坏。很多混凝土结构未到服役寿命就产生各种非力学原因引起的破坏，导致高昂的混凝土维修费，因此混凝土的硫酸盐腐蚀问题受到愈来愈多的关注[4~7]