碱激发粉煤灰和矿渣对疏浚淤泥改性影响 　　摘要：针对我国湖泊淤泥处置和利用的现状，本文设想利用激发剂激发粉煤灰和矿渣来改性疏浚淤泥，以发现激发剂对疏浚淤泥改性的影响。通过实验证实，淤泥加入固化剂固化改性以后，使其更加接近工程土的性质，可以作为目前大规模的土木工程建设的工程材料，进而丰富淤泥的处理方式，使淤泥的处理变废为宝。 　　关键词：湖泊淤泥、激发剂、粉煤灰、矿渣、力学特性 　　 　　The effect of alkali activation of fly ash and slag on dredging sludge modification 　　Yin Jingxin, Yu Pingping 　　（Environmental and civil engineering institute，Jiangnan University,Wuxi, 214000,China) 　　Abstract:For the current situation of the disposal and utilization of Lake mud in our country,this article envisaged in using excitant to excite fly ash and slag to modification the dredged silt,and to find the influence for it by the excitant.The experiment confirm that sludge by adding a curing agent modified to make it closer to the nature of engineering soil can be used as engineering materials for large-scale civil engineering construction, and thus rich sludge handling, sludge processing waste into treasure. 　　Keywords:Lake mud, excitant, fly ash, slag, mechanical property 　　中图分类号：K928.43 文献标识码：A 文章编号： 　　 　　 　　引 言 　　河道、湖泊及城市淤泥是一种重要的矿产资源。由于缺少对这些淤泥的研究，其潜在价值一直未被发现，而随着社会的快速发展，各种资源逐渐紧缺的情况下，淤泥作为矿产资源对社会的可持续发展有着重大的作用。目前国内处理疏浚淤泥多为堆积或填埋，不仅占用土地还会造成二次污染。开发利用疏浚淤泥，可以净化水域，改善水质，变废为宝，造福一方。 　　本文通过利用碱激发粉煤灰和矿渣来改性疏浚淤泥，以发现激发剂对疏浚淤泥改性的影响。试验在不同的激发剂掺加量,不同的养护时间下等结果发现，经改性后的淤泥其抗剪强度有了很大的提高，显微结构也有所变化,出现水化产物，土体趋于紧密。淤泥加入固化剂固化改性以后，使其更加接近工程土的性质，可以作为目前大规模的土木工程建设的工程材料。 　　 　　1 实验材料 　　本试验采用淤泥作为原料土，粉煤灰、水泥和矿渣以及一些NaOH等化学添加剂作为固化材料，来研究不同固化材料掺入量及种类对淤泥质土的固化效果。试验过程中具体涉及的材料有：粉煤灰、矿渣、水泥、水、淤泥等。淤泥中的粘粒(粒径 　　由期龄和NaOH 的含量综合比较，可以看出当NaOH 的含量为0.35%时对粉煤灰和矿渣的激发效果比较好，在期龄为28天时效果最好的工况S26F26N0.35在正应力300kpa时剪应力达到416 kpa。 　　 　　3疏浚淤泥的显微结构研究 　　 　　 图3-1原状土SEM图像 　　图3-1是原状淤泥的显微结构图片。从图中我们可以看到很多片状的粘土矿物。颗粒间连接不紧密，存在较多的孔隙，且有的孔隙比较大。这也在微观结构上解释了原状淤泥强度低、稳定性差的原因。 　　 　　图3-2 NaOH掺量为0.35%的SEM图像 　　从图3-2中我们可以十分明显地看到许多棒状的水化产物，对土颗粒进行了胶结，反应在宏观上，改性淤泥的强度将提高。这点在直剪数据上得到了一定的印证。也符合之前作出的推测，即加了水泥的工况在NaOH掺量为0.35%抗剪强度最高。 　　从上图我们也可以看到一些针状的水化产物，说明NaOH对粉煤灰和矿渣的激发还是很有效果的，也符合之前的推断。由此我们可以确定：碱的掺入对淤泥土性的完善有较为明显的作用。 　　 　　4结论 　　加了水泥的那组工况的抗剪强度每个期龄都有一