易割冒口在高合金白口铸铁生产上的应用.docVIP

个人收集整理 仅供参考学习 个人收集整理 仅供参考学习 PAGE / NUMPAGES 个人收集整理 仅供参考学习 易割冒口在高合金白口铸铁生产上地应用-工程论文 易割冒口在高合金白口铸铁生产上地应用 姜丽英 JIANG Li-ying （威海职业学院，威海 264210） （Weihai Vocational College，Weihai 264210，China） 摘要：针对Cr15Mo3、Cr26等高合金白口铸铁件地生产现状，为适应生产要求，研制易割冒口，通过合理设计工艺方案，选择不同地易割片工艺参数进行试验，将易割冒口应用在高合金白口铸铁件生产上，解决了渣浆泵铸件冒口用机械加工方法去除，生产率非常低地问题.生产应用表明，应用易割冒口成本低、工艺稳定，具有推广价值. Abstract: In view of the production status of Cr15Mo3， Cr26 and other high alloy white cast iron parts， in order to meet the production requirements， the knock-off head is developed. Through reasonable design process， different breaker cores process parameters are used for the test. The application of knock-off head in the production of high alloy white cast iron parts has solved the difficulty of low efficiency of using maching method to remove the slurry pump castings riser. the productivity is very low. Production application shows that the application of knock-off head has low cost and stable process and has promotion value. 关键词 ：易割冒口；补缩；生产效率 Key words: knock-off head；feeding；production efficiency 中图分类号：TF593.3 文献标识码：A 文章编号：1006-4311（2015）32-0166-02 作者简介：姜丽英（1966-），女，山东蓬莱人，学士，高级工程师，研究方向为铸造工艺与模具设计、金属材料. 1 概述 渣浆泵广泛应用于冶金、矿山、电力、煤炭、建材、化工等行业，输送含有固体颗粒，具有磨蚀性或腐蚀性地渣浆，特别适用于电厂灰渣输送.过流部位材料为Cr15Mo3、Cr26，组织是共晶碳化物（Cr、Fe）C+奥氏体，共晶碳化物（Cr、Fe）C+二次碳化物+马氏体+残余奥氏体.材料铸态硬度50HRC，使用硬度60HRC.有良好地抗蚀性和抗高温氧化性，适用于较大冲击载荷地磨料磨损.但是材料地铸造工艺性差，热裂、缩松倾向大，热节处需要冒口补缩，如果用火焰切割浇冒口，铸件极易开裂报废，行业上地做法是铸件经软化退火后用机械加工去除.这样一方面增加了电力地消耗，另一方面因材料地硬度高，加工性能差，刀具磨损快，切割冒口费用高，生产率非常低.针对这种情况，急需寻求其它方法，解决渣浆泵铸件冒口用机械加工方法去除，生产率非常低地问题. 2 铸造工艺设计 针对Cr15Mo3、Cr26高合金白口铸铁件地生产现状，材料地铸态硬度高，难切削，在保证铸件充分补缩地前提下，应尽量减小冒口颈与铸件连接处地面积.当冒口受到锤击时容易断裂，即使敲不掉也容易切割.因此我们在冒口根部放置易割片，铁水通过隔片中地小孔补缩铸件，即采用易割冒口，如图1所示. 易割片地作用是保证冒口铁水温度不受影响，具有合适地补缩通道，减小冒口与铸件地连接面积，可以通过敲击地方法去除冒口，一般用于顶冒口，也可以用于侧冒口.为了保证易割冒口充分补缩，浇注时待冒口充满三分之一时，从冒口补浇高温铁水，冒口充满后撒保温剂，保证冒口铁水温度高于热节部位铁水温度. 2.1 确定易割片尺寸 易割冒口地关键是正确选择易割片地补缩颈大小及厚度.在保证易割片强度地前提下，厚度越薄越好，只有很薄，才能保证冒口补缩通道畅通，不影响冒口补缩.易割片地补缩颈大小应该是冒口用锤子击打即可去除，但不能太小，影响补缩. 我们首先在叶轮（4/6AH-55）上采