金属结构件残余应力超声波测量及优化技术3.ppt

金属结构件残余应力的超声波测量及优化技术 残余应力测试方法 总结 感谢您的关注！ 北京康坦科技有限公司 联系电话：010 网址： 原理示意图 UP技术的作用 增加疲劳寿命和疲劳强度 消除精密部件的焊接变形 增加耐腐蚀性 增加显微硬度 表面纳米化（纳米晶） Gary B. Marquis From: Gary B. Marquis Presented at Commission XIII Fatigue behavior of welded structures, International Institute of Welding 优化前后对接焊缝的变化 焊后状态 使用UP技术后 30mm 15mm 优化前后角焊缝的变化 UP技术在管焊接接头的应用 1 - in as-welded condition for all types of steel 3, 5, 7 and 9 - after application of the UP to Steel 1, Steel 2, Steel 3 and Steel 4 Low and High Strength Steels Aluminum and its alloys Titanium and its alloys For high loads (700 MPa) of fuselage endurance increase Welded Plastics UP技术可以用于多种材料 UP技术对疲劳寿命的影响 Drawings of welded specimens for fatigue testing at different conditions W – as-welded condition; R - repair by gouging and welding; R/UP – repair by gouging, welding and UP 1 - as-welded condition, 2, 3 and 4 – after first, second and third weld repair 5, 6 and 7 - after first, second and third weld repairwith application of UP I - fatigue crack is repaired by gouging and welding, II - fatigue crack is repaired by gouging, welding and UP, III – UP is applied before/during the first phase of service life, W – as-welded condition, R - repair by gouging and welding, R/UP – repair by gouging, welding and UP W/UP- welding and UP A2 Steel HSLA Material Not treated by UP After UP treatment Not treated by UP After UP treatment UP技术对金属腐蚀的影响 Surface hardness of automotive engine valves UP技术对表面硬度的影响 消除由于焊接产生的扭曲变形 使用UP技术，可以消除由于焊接产生的扭曲变形 6mm厚钢板 优化前 优化后 通过UP技术，可以使材料表面形成纳米晶，约几μm 厚。 实现表面纳米化 UP技术的优点 效率高（最高） 快速(每分钟约处理 0.5 m 焊缝) 大大减少振动和噪音，操作简单 渗透更深 计算机控制 机器人在线应用 与类似的磁致伸缩系统相比，更轻巧，无需强制水冷 UP已经成功的应用于提高焊接件疲劳寿命，抗腐蚀性，消除由于焊接和其他工艺引起的塑性变形，消除残余应力，增加材料表面硬度和表面纳米化。主要应用领域有：铁路和高速公路桥，矿业，施工机械，船舶制造，汽车和航空航天。 应用案例 高速公路铁路桥梁焊接件： 一个100mm长的焊缝，经过UP处理，焊接件疲劳寿命显著地增加，并且可以消除疲劳裂纹的产生。 在修复整段俄亥俄河大桥高速公路桥的过程中，UP处理了大约500m长的焊缝，超过2000个疲劳关键点的焊接件。 焊接桥梁上的应用 UP of Fatigue Critical Welds of a Grinding Mill 修复采矿设备上的应用 UP of a Welde