CSP轧辊表面缺陷原因分析及对策.pdf

邯钢 CSP 轧辊表面缺陷原因分析及对策 杨付勇 田吉祥 王春生 赵艳良 （河北钢铁集团邯钢公司连铸连轧厂，邯郸 056015 ） 1 摘 要 轧辊的表面质量与工作环境和工作状态以及自身的材质特性有着紧密的联系，热轧板带生产中的轧辊表面 质量缺陷对最终产品的质量造成了不同影响。轧辊表面质量缺陷形式主要包括氧化膜脱落、过渡磨损、振痕、热疲 劳、表面拉伤、支承辊疲劳裂纹等。本文介绍了轧辊在热轧板带生产中表现出来的各种表面缺陷，并对其成因进行 了具体分析，同时提出了相应解决措施，以及现场的实际使用情况。 关键字 轧辊 表面缺陷 工作辊 支承辊 The Defect of Rolls Surface and Solve Method in HanGang CSP Plant Yang Fuyong Tian Jixiang Wang Chunsheng Zhao Yanliang (CSP Plant, Handan Iron and Steel company, Hebei Iron and Steel Group，Handan, 056015) Abstract Roll surface quality and work environment and working state and its own material characteristic are closely linked, in the production of the hot rolled strip below surface defects caused by quality to the end product of the different effects. Roll surface quality defect forms including oxidation film falls off, transition wear, vibration mark, thermal fatigue, surface strain, supporting roller fatigue crack, etc. This paper introduced the form cause about lacuna of rolls surface in hot strip, and we also gave the analyse and the solve measure, and the application in workplant. Key words roll, surface lacuna, work roll, bur roll 1 引言 轧辊是轧钢生产过程中关键性的工艺备件，对产品质量的提高和生产成本的降低都有着很大影响。轧辊 的表面状况与工作环境和工作状态以及自身的材质特性有着紧密的联系，热轧板带生产中的轧辊表面缺陷对 最终产品造成了不同影响。本文对生产中的不同轧辊表面缺陷进行了具体描述，并对其成因进行了分析，同 时提出了相应解决措施。 2 轧辊表面缺陷形式及对应解决措施 轧辊表面缺陷形式主要包括以下几个方面：工作辊氧化膜脱落、过渡磨损、走刀痕和振痕、热疲劳、表 面拉伤及支承辊疲劳裂纹等。 2.1 氧化膜脱落 表面氧化膜的形成并不是在上机期间均匀产生的，其基本上取决于：轧辊材质、轧制工艺条件，如轧制 温度、变形速度及程度、工作辊冷却状况、轧制节奏、轧辊与轧件接触区的摩擦条件等。 杨付勇，男，工程师，从事轧钢专业，tjx318@ 邯钢CSP 轧辊表面缺陷原因分析及对策 8-75 在轧制过程中，交变摩擦力及交变热负荷超过了轧辊辊身材质的热疲劳剪切强度，氧化膜在最初的形成 区域内扩展蔓延直至从轧辊上脱落。一旦辊