含锌粉尘造电弧炉泡沫渣的研究.pdf

第 24 卷第 5 期 　　　 特殊钢 　 Vol . 24 . No . 5 　　　　 2003 年 9 月 　　　　　　　 SPECIAL STEEL 　 September 　2003 　　　　 ·25 · 含锌粉尘造电弧炉泡沫渣的研究 　 王 　涛 　朱立新 　 　　陈伟庆 　梁 　君 　郭汉杰 ( ) ( ) 宝钢研究院 ,上海 201900 　 　 北京科技大学 ,北京 100083 摘 　要 　对宝钢含锌高炉粉尘 、转炉二次除尘灰和电弧炉粉尘按不同配比造块与沥青焦粉混合后加入 电弧炉熔渣 ,研究了粉尘和沥青焦加入量对炉渣发泡高度和维持时间的影响 。结果表明 ,加入粉尘有利于炉 渣发泡 ,炉渣中分别加入 5 %～10 %沥青焦和 20 %粉尘压块时 ,其发泡效果最佳 。 关键词 　含锌粉尘 　电弧炉 　泡沫渣 An Investigation on ZnO Bearing Dusts Recycling Utilization for Arc Furnace Slag Foaming Wang Tao and Zhu Lixin ( Technical Center , Baoshan Iron and Steel Co Ltd , Shanghai 201900) Chen Weiqing , Liang Jun and Guo Hanj ie (University of Science and Technology , Beijing 100083) Abstract 　The effect of adding amount of dusts and pitch coke on slag foaming height and maintaining time has been investigated by adding pitch coke with ZnO bearing blast furnace dust , converter secondary removing dust and arc furnace dust at Baoshan for arc furnace slag foaming. The test results showed that added dusts was favourable to arc furnace slag foaming , and foaming effect was optimum with adding 5 %～10 % pitch coke and 20 % dusts briquette in slag. Material Index 　ZnO Bearing Dust , Arc Furnace , Foaming Slag 　　宝钢每年产生大量的高炉瓦斯泥 、转炉二次 测量泡沫渣高度时 ,预先在渣中插入细刚玉 (Φ ) 除尘灰和电炉粉尘因含锌得不到利用 ,造成严重 棒 5 mm , 目测炉渣发泡情况 ,待达到最大高度 的环境污染和二次资源的浪费 。高炉瓦斯泥含有