PAGE PAGE IV 二亚胺镍催化甲基丙烯酸甲酯的聚合研究 PAGE III 二亚胺镍催化甲基丙烯酸甲酯的聚合研究 摘要 镍系催化是一种重要的烯烃聚合的催化剂体系，成为现今应用最广泛的催化体系之一，在化工合成中具有重要的地位。 本课题用二亚胺镍作为催化剂，以甲基铝氧烷为助催化剂，研究了甲基丙烯酸甲酯的聚合，并通过实验结果分析Al/Ni摩尔比、反应时间、反应温度对聚合产率的影响进行了研究，最后对合成的聚合物的结构进行了表征。聚合结果表明，不同的实验条件对产率的影响很大。通过实验得到的合成聚甲基丙烯酸甲酯的最佳条件为：Al/Ni摩尔比500、反应时间10小时、反应温度60oC，聚合物的最高产率为80.72％。 关键词：二亚胺镍；甲基丙烯酸甲酯；催化剂；聚合 Polymerization of Methyl Methacrylate with Diimine Nickel Catalyst Abstract Nickel complex is an important olefin polymerization catalyst systems, it become one of the most widely used catalytic system that has important role in chemical industry. The paper studies the polymerization of methyl methacrylate with diimine nickel as a catalyst in the presence of MAO. The effect of the Al/Ni molar ratio, the reaction time and the reaction temperature on the yield of polymerization was studied. The structure of the obtained PMMA was characterized by NMR and IR. The results show a significant influence of the experimental conditions on the yield of polymer. The optimal condition for the synthesis of PMMA is Al/Ni molar ratio of 500. the reaction time is 10 hours at 60oC, highest yield of PMMA is 80.72％. Keywords: diimine nickel; methyl methacrylate; catalyst; polymerization 目 录TOC \o 1-3 \h \u 9203 1 绪论 1 17340 1.1后过渡金属催化剂 1 30094 1.1.1后过渡金属催化剂在聚合中的应用 1 21700 1.1.2 α-二亚胺配体的发展 2 8336 1.2镍系催化剂 2 27281 1.2.1二亚胺镍的特点 3 1874 1.3甲基丙烯酸甲酯的合成 3 30706 1.3.1聚甲基丙烯酸甲酯的发展历史和产业现状 3 27607 1.3.2聚甲基丙烯酸甲酯的特点及应用 4 12172 1.3.3甲基丙烯酸甲酯的聚合工艺 4 29749 1.4聚甲基丙烯酸甲酯分子量的控制 6 27922 1.4.1控制聚甲基丙烯酸甲酯分子量的措施 6 2913 1.5本课题的研究背景及内容 7 15728 2 实验部分 9 18749 2.1引言 9 9503 2.2试剂和表征仪器 9 9229 2.3表征手段 9 32310 2.3.1 IR-红外光谱分析 9 32462 2.3.2 1H- NMR -核磁共振氢谱分析 10 21501 2.3.3 DSC谱图分析 10 765 2.4聚合物的合成 10 4099 2.4.1聚合实验方案设计 10 27085 3 结果分析与讨论 12 11533 3.1实验数据记录 12 14306 3.2 聚甲基丙烯酸甲酯的红外图谱分析 13 1624 3.3 聚甲基丙烯酸甲酯的核磁图谱分析 14 18438 3.4 聚甲基丙烯酸甲酯的差热图谱分析 16 19967 4结论 17 9338 参考文献 18 PAGE PAGE 2