不锈钢手术器械真空钎焊与热处理复合工艺的应用.docx

~工艺~

00

不锈钢手术器械真空钎焊与热处理复合工艺的应用

鲍国华

(上海医疗器械(集团)有限公司手术器械厂，上海200072)

摘要：为了提高某些不锈钢手术器械的耐磨性和防滑性能，要对其进行真空钎焊硬质合金与淬火相结合的复合处理。主要工艺参数为：最高加热温度1320℃,极限真空度4×10-1Pa,最大气淬压力0.6MPa。这种复合工艺具有被处理产品质量好，能耗低，生产率高，作业环境改善等特点。

关键词：不锈钢手术器械；真空钎焊；淬火

中图分类号：TG454;TG156.95文献标识码：B文章编号：1008-1690(2013)06-0044-03

ApplicationofConjuctionofVacuumBrazingwithHeatTreatment

toSurgicalInstrumentofStainlessSteel

BAOGuohua

(SurgicalInstrumentsFactory,ShanghaiMedicalInstruments(Group)Co.,Ltd.,Shanghai200072,China)

Abstract:Certainsurgicalinstrumentsaretobecompositelytreatedbyaprocessconsistingofvacuumbrazingcementedcarbidefollowedbyquenchingtoimproveontheirwearresistanceanddeslickingability.Themainprocessparametersare:thehighestheattemperatureof1320℃,thehighestvacuityof4×10-1Paandthemaximumgasquenchingpressureof0.6MPa.Thistypeofcompositeprocesspossessessuchfeaturesasbetterqualityofproductstreated,lowerenergyconsumption,higherproductionefficiencyandimprovedoperatingplace.Keywords:surgicalinstrumentofstainlesssteel;vacuumbrazing;quenching

一种用于夹持缝针及打结的手术器械，在其工作端采用镶嵌技术镶入硬质合金，以获得更好的耐磨、防滑性能及便于维修更换。近年来，我厂在此类产品上采用真空钎焊热处理复合工艺，即将原真空钎焊与真空热处理二道工序合二为一，取得了一定的效果，见图1。本文就真空钎焊热处理复合工艺的应用作一些介绍和探讨。

1工艺方法及材料成分

产品原先的加工工序：机械加工→淬火→工作端高频焊接→表面处理→检验。这种工艺流程的缺点是：工件经过整体淬火后再作局部焊接，焊接热会改变工件的局部组织状态，不仅影响产品的力学性能和耐腐蚀性能，也影响产品的使用性能；其次，焊

不锈钢

(a)钎焊前(b)钎焊后

(a)Beforebrazing(b)Afterbrazing

图1一种手术器械钎焊硬质合金的示意图

Fig.1Schemeofbrazingcementedcarbidetoasurgicalinstrument

收稿日期：2012-08-06

作者简介：鲍国华(1960-),男，浙江镇海人，高级工程师，已发表论文7篇。联系电话：0212002,E-mail:bghok@

·44·《热处理》2013年第28卷第6期

接基本是手工操作，质量控制难度大；再次，焊接与热处理分开操作，工期长，能耗高。改进后的加工工序为：机械加工→真空钎焊/淬火→表面处理→检验。其中主要改进之处在于采用钎焊+淬火的复合工艺，即焊接和热处理同时完成，除降低能耗、提高

工效、改善作业环境外，还克服了原有工艺的品质缺陷。工件基体材料为20Cr13钢；硬质合金为K40,相当于YG11,