抗菌聚酰胺复合纳滤膜的制备及表征

张宇峰;李文俏;潘赢;张雯;孟建强

【摘要】Inordertoimprovetheantibacterialpropertyofthecomposite

membrane,anantibacterialcompositepolyamidenanofiltration

membranewaspreparedviatheinterfacialpolymerizationusingthe

branchedpolyethyleneimine(PEI)asanaqueousmonomer,trimesoyl

chloride(TMC)asanorganicphasemonomer,onthesurfaceof

polysulfoneultrafiltrationmembrane.Theeffectsofdifferentpreparation

conditionsonthemembranepropertieswerestudied.Itwasfoundthat

whenPEIcontentwas1.5％,TMCcontentwas0.2％,reactiontimewas5

min,thePEI/TMCcompositemembraneobtainedthebestperformance.It

showedthemembranerejectionto0.1％MgSO4was95％,thefluxwas

about55L/(m2·h)whenitwastestedat25℃,1.5MPa.Gram-negativeE.

coliandGram-positiveS.aureuswereusedasthebacterialmodelto

evaluatetheantibacterialpropertiesofthemembranesusingshakeflask

method.ThePEI/TMCmembranehasverygoodantibacterialpropertyand

theantibacterialratereaches70％-95％forbacteriawithaconcentration

of103CFU/mL.%为了提高复合膜的抗菌性能,以聚砜超滤膜为基膜,以超支化聚

乙烯亚胺(PEI)为水相单体,以均苯三甲酰氯(TMC)为有机相单体,制备出

PEI/TMC抗菌性聚酰胺复合纳滤膜,并探究复合膜渗透性能和抗菌性能.结果显示:

当PEI质量分数为2％、TMC质量分数0.1％、反应时间为5min时,在1.5MPa、

25℃的条件下过滤0.1％的MgSO4溶液,得到的膜渗透选择性能最佳,此时通量

为55L/(m2·h),截留率为95％;以革兰氏阴性菌大肠杆菌以及革兰氏阳性菌金黄

色葡萄球菌为细菌模型,采用接触振荡法进行测试,证明了PEI/TMC相比于传统的

商品聚酰胺复合膜,具有非常好的抗菌性,对于浓度为103CFU/mL左右的细菌,抑

菌率可达到70％～95％.

【期刊名称】《天津工业大学学报》

【年(卷),期】2019(038)001

【总页数】6页(P1-6)

【关键词】聚酰胺;超支化聚乙烯亚胺;纳滤膜;抗菌;薄层复合膜;界面聚合

【作者】张宇峰;李文俏;潘赢;张雯;孟建强

【作者单位】天津工业大学省部共建分离膜与膜过程国家重点实验室,天津

300387;天津工业大学材料科学与工程学院,天津300387;天津工业大学省部共建

分离膜与膜过程国家重点实验室,天津300387;天津工业大学材料科学与工程学院,

天津300387;天津工业大学省部共建分离膜与膜过程国家重点实验室,天津

300387;天津工业大学材料科学与工程学院,天津300387;天津工业大学省部共建

分离膜与膜过程国家重点实验室,天津300387;天津工业大学材料科学与工程学院,

天津300387;天津工业大学省部共建分离膜与膜过程国家重点实验室,天津

300387;天津工业大学材料科学与工程学院,天津300387

【正文语