X70M高频焊管胀环试验性能研究

梁才萌;裴银柱;张坤鹏;张荣胜;李文平

【摘要】为了准确测量钢管的屈服强度,以Φ323.9mm×6.4mm、材质为X70M

的高频焊管为例,对钢管防腐前后的板状试样和环形试样分别进行了拉伸试验和胀

环试验,并分析对比了试验结果.结果表明,板状试样相对于环形试样的屈服强度出现

了较大的波动,其原因是板状拉伸试验在试样展平过程中发生了包申格效应和加工

硬化.防腐后钢管的胀环试验结果明显高于防腐前,其原因是防腐涂敷过程中钢管经

受时效热处理产生了时效强化作用.另外因焊缝与管体的组织不同,造成胀环试验后

两者的变形量明显不同,因此使用胀环试验测量管体的屈服强度不够合理.%In

ordertoaccuratelydetecttheyieldstrengthofsteelpipe,takingX70M

Φ323.9mm×6.4mmhigh-frequencyweldedpipeasanexample,the

tensiletestandexpansionringtestonplatespecimenandring-shaped

specimenwereconductedrespectivelybeforeandafteranticorrosionof

steelpipe,andthetestresultswereanalyzedandcompared.Theresults

showedthatrelativetothering-shapedsample,theyieldstrengthofthe

platespecimenappearedgreatfluctuation,andthereasonwasthatthe

Bauschingereffectandworkhardeningoccurredinplatetensilespecimen

flatteningprocess.Theexpansionringtestresultafteranticorrosionwas

obviouslyhigherthanthatofbeforeanticorrosion,thereasonwasthat

duringsteelpipecoatingprocess,theagingreinforcementeffect

occurrencecausedbyagingheattreatment.Inaddition,becausethe

microstructureofweldandpipebodywasdifferent,thedeformation

amountofweldandpipebodywassignificantlydifferentafterexpansion

ringtest.Therefore,usingexpansionringtesttomeasuretheyieldstrength

ofpipebodyobviouslywasnotreasonable.

【期刊名称】《焊管》

【年(卷),期】2017(040)009

【总页数】5页(P16-20)

【关键词】焊管;高频焊管;屈服强度;胀环试验;环形试样;板状拉伸

【作者】梁才萌;裴银柱;张坤鹏;张荣胜;李文平

【作者单位】番禺珠江钢管(连云港)有限公司,江苏连云港222006;番禺珠江钢管

(连云港)有限公司,江苏连云港222006;番禺珠江钢管(连云港)有限公司,江苏连云

港222006;番禺珠江钢管(连云港)有限公司,江苏连云港222006;番禺珠江钢管(连

云港)有限公司,江苏连云港222006

【正文语种】中文

【中图分类】TG407

屈服强度是油气输送管道钢管力学性能的重要指标，相关的产品标准有APISPEC

5L：2012[1]、GB/T9711—2011[2]、ISO3183—2012[3]、CSAZ245.1—

2007[4]、DNV-OS-F101—2013[5]以及DEP31.40.20.37—2011[6]等。这些标

准规定可以采用板状或圆棒试样的拉伸试验来检测屈服强度，一般取规定总延伸率

为0.5%时的应力Rt0.5