位错dislocation

相图phasediagram

相律phaserule

形核率nucleationrate

亚共析钢hypo-eutectoidsteel

一次键primarybonding

应变时效strainaging

硬度hardness

原子堆垛结构atompackedstructure

匀晶相图isomorhousphasediagram

再结晶recrystallization

枝晶偏析dendriticsegregation

中间相intermediatephase

珠光体pearlite

位错钉扎anchoringofdislocations

吴氏网Wulffnet

体心立方结构body-centeredcubiccrystalstructure

铁素体ferrite

三元相图ternaryphasediagrams

氢键hydrogenbonding

驱动力drivingforce

二次键secondarybonding

固相线solidus

固溶体solidsolution

合金alloy

滑移slip

回复recovery

间隙固溶体interstitialsolidsolution

晶胞unitcells

浓度梯度concentrationgradient

扩散diffusion

柯氏气团Cottrellatmoshere

凝固Soliddiffcation

孪晶twins

奥氏体austenite

柏氏矢量Burger‘svector

残余应力residualstress

塑性形变plasticdeformation

点缺陷pointdefect

刃型位错edgedislocation

41．小角度晶界low-anglegrainboudary

42．同素异构allotropy

43．渗碳体ironcarbide

44．屈服yielding

45．共晶白口铸铁eutecticwhitecastiron

46．固溶强化sloid-solutionstrengthening

47．晶粒长大graingrowth

48．晶向族afamilyofcrystaldirections

49．杠杆定律leverrule

50．形核nucleation

图像1.根据下列条件画出一个二元系相图，A和B的熔点分别是1000℃和700℃，含wB=25%的合金正好在500℃完全凝固，它的平衡组织由73.3%的先共晶。和26.7%的(α+β)共晶组成。而wB＝50%的合金在500℃时的组织由40%的先共晶α和60%的(α+β)共晶组成，并且此合金的α总量为50%。

答案：

图像2.作图表示立方晶体的晶面及晶向。

答案：

图像3.三元相图投影图如图所示，请在分别在图(b)(c)(d)中标出各垂直截面中各相组成

答案：

简答4.判断下列位错反应能否进行，请说明原因。

1)2)

3)4)

答案：(1)能。(2)不能(3)不能(4)不能

简答5.写出立方晶体中晶面族{100}，{110}，{111}，{112}等所包括的等价晶面。

答案：{100}＝(100)十(010)+(001)，共3个等价面。

{110}＝(110)十()+(101)+()+(011)+()，共6个等价面。

{111}＝(111)+()+()+()，共4个等价面。

共12个等价面。

计算6.纯Cu的空位形成能是1.5aJ/atom(1aJ=10-18J)，将纯Cu加热到850℃后激冷到室温（20℃），如果高温下的空位全部保留，试求过饱和空位浓度与室温平衡空位浓度的比值。（玻尔兹曼常数K=1.38×10^-23J/K）

简述7.铸件组织有何特点？

答案：在铸锭组织中，一般有三层晶区：（1）最外层细晶区。其形成是由于模壁的温度较低，液体的过冷度交大，因此形核率较高。（2）中间为柱状晶区。其形成是由于模壁的温度升高，晶核的成长速率大于晶核的形核率，且沿垂直于模壁风向的散热较为有利。在细晶区中取向有利的晶粒优先生长为柱状晶粒。（3）中心为等轴晶区。其形成是由于模壁温度进一步升高，液体过冷度进一步降低，剩余液体的散热方向性已不明显，处于均匀冷却状态；同时，未熔杂质、破断枝晶等易集中于剩余液体中，这些都促使了等轴晶的形成。应该指出，铸锭的组织并不是都具有3层晶区。由于凝固条件的不同，也会形成在铸锭中只有某一种晶区，或只有某两种晶区。

简述8.比较说明过冷度、临界过冷度、动态过冷度等概念的区